VALOX™ FR Resin 310SE0 - Americas
聚丁烯对苯二甲酸酯
产品说明:
VALOX 310SE0 is an unreinforced, flame retardant Polybutylene Terephthalate (PBT) injection moldable grade with excellent chemical resistance. It has a UL94V0@0.71mm and 5VA@3.0mm flame rating. This is a good candidate for thin wall applications in the electrical industry including bobbins, keyboards, switches and appliance housings.
|
材料状态
|
|
|
UL 黄卡 1
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
用途
|
|
|
多点数据
|
- Elastic Modulus vs Temperature (ASTM D4065)
- Flexural DMA (ASTM D4065)
- Instrumented Impact (Energy) (ASTM D3763)
|
- Instrumented Impact (Load) (ASTM D3763)
- Specific Heat vs. Temperature (ASTM D3417)
|
- Tensile Creep (ASTM D2990)
- Tensile Stress vs. Strain (ASTM D638)
|
|
|
Also Available In
|
|
|
密度 / 比重
|
|
|
|
|
--
|
1.40
|
|
ASTM D792 |
|
--
|
1.40
|
g/cm³
|
ISO 1183 |
|
特定体积
|
19.7
|
in³/lb
|
ASTM D792 |
|
熔流率（熔体流动速率） (250°C/2.16 kg)
|
8.6
|
g/10 min
|
ASTM D1238 |
|
熔融体积流量（MVR） (250°C/2.16 kg)
|
8.0
|
cm³/10min
|
ISO 1133 |
|
收缩率
|
|
|
内部方法 |
|
垂直 2
|
0.90 到 1.9
|
%
|
|
|
流动 2
|
1.1 到 1.8
|
%
|
|
|
垂直 : 0.0295 到 0.0906 in
|
1.0 到 1.7
|
%
|
|
|
流动 : 0.0295 到 0.0906 in
|
0.90 到 1.6
|
%
|
|
|
流动 : 0.126 in
|
1.5 到 2.3
|
%
|
|
|
垂直 : 0.0906 到 0.181 in
|
1.6 到 2.4
|
%
|
|
|
流动 : 0.0906 到 0.181 in
|
1.5 到 2.3
|
%
|
|
|
吸水率
|
|
|
ISO 62 |
|
饱和, 73°F
|
0.36
|
%
|
|
|
平衡, 73°F, 50% RH
|
0.080
|
%
|
|
|
洛氏硬度 (R 计秤)
|
120
|
|
ISO 2039-2 |
|
球压硬度 (H 358/30)
|
15200
|
psi
|
ISO 2039-1 |
|
拉伸模量
|
|
|
|
|
-- 3
|
409000
|
psi
|
ASTM D638 |
|
--
|
406000
|
psi
|
ISO 527-2/1 |
|
抗张强度
|
|
|
|
|
屈服 4
|
8410
|
psi
|
ASTM D638 |
|
屈服
|
8410
|
psi
|
ISO 527-2/50 |
|
断裂 4
|
7540
|
psi
|
ASTM D638 |
|
断裂
|
5800
|
psi
|
ISO 527-2/50 |
|
伸长率
|
|
|
|
|
屈服 4
|
5.0
|
%
|
ASTM D638 |
|
屈服
|
5.0
|
%
|
ISO 527-2/50 |
|
断裂 4
|
18
|
%
|
ASTM D638 |
|
断裂
|
18
|
%
|
ISO 527-2/50 |
|
弯曲模量
|
|
|
|
|
1.97 in 跨距 5
|
380000
|
psi
|
ASTM D790 |
|
-- 6
|
377000
|
psi
|
ISO 178 |
|
弯曲应力
|
|
|
|
|
-- 6, 7
|
13100
|
psi
|
ISO 178 |
|
屈服, 1.97 in 跨距 5
|
14600
|
psi
|
ASTM D790 |
|
泰伯耐磨性 (1000 g, CS-17 转轮)
|
19.0
|
mg
|
内部方法 |
|
简支梁缺口冲击强度
|
|
|
|
|
-22°F 8
|
1.9
|
ft·lb/in²
|
ISO 179/1eA |
|
73°F 8
|
3.8
|
ft·lb/in²
|
ISO 179/1eA |
|
73°F
|
2.4
|
ft·lb/in²
|
ISO 179/2C |
|
简支梁无缺口冲击强度 8
|
|
|
ISO 179/1eU |
|
-22°F
|
无断裂
|
|
|
|
73°F
|
无断裂
|
|
|
|
悬壁梁缺口冲击强度
|
|
|
|
|
-22°F
|
0.47
|
ft·lb/in
|
ASTM D256 |
|
73°F
|
0.75
|
ft·lb/in
|
ASTM D256 |
|
-22°F 9
|
1.9
|
ft·lb/in²
|
ISO 180/1A |
|
73°F 9
|
2.4
|
ft·lb/in²
|
ISO 180/1A |
|
无缺口悬臂梁冲击
|
|
|
|
|
73°F
|
无断裂
|
|
ASTM D4812, ISO 180/1U |
|
-22°F 9
|
无断裂
|
|
ISO 180/1U |
|
装有测量仪表的落镖冲击 (73°F, Total Energy)
|
1770
|
in·lb
|
ASTM D3763 |
|
载荷下热变形温度
|
|
|
|
|
66 psi, 未退火, 0.252 in
|
324
|
°F
|
ASTM D648 |
|
66 psi, 未退火, 0.157 in, 3.94 in 跨距 10
|
302
|
°F
|
ISO 75-2/Be |
|
264 psi, 未退火, 0.126 in
|
165
|
°F
|
ASTM D648 |
|
264 psi, 未退火, 0.252 in
|
160
|
°F
|
ASTM D648 |
|
264 psi, 未退火, 0.157 in, 3.94 in 跨距 10
|
140
|
°F
|
ISO 75-2/Ae |
|
264 psi, 未退火, 0.157 in, 2.52 in 跨距 9
|
163
|
°F
|
ISO 75-2/Af |
|
维卡软化温度
|
|
|
|
|
--
|
338
|
°F
|
ASTM D1525 11, ISO 306/B120, ISO 306/B50 |
|
--
|
414
|
°F
|
ISO 306/A50 |
|
Ball Pressure Test (253 到 261°F)
|
通过
|
|
IEC 60695-10-2 |
|
线形热膨胀系数
|
|
|
|
|
流动 : -40 到 104°F
|
4.4E-5
|
in/in/°F
|
ASTM E831 |
|
流动 : 140 到 280°F
|
7.3E-5
|
in/in/°F
|
ASTM E831 |
|
流动 : -40 到 104°F
|
4.2E-5
|
in/in/°F
|
ISO 11359-2 |
|
流动 : 73 到 140°F
|
5.6E-5
|
in/in/°F
|
ISO 11359-2 |
|
垂直 : -40 到 104°F
|
4.4E-5
|
in/in/°F
|
ASTM E831 |
|
垂直 : -40 到 104°F
|
4.1E-5
|
in/in/°F
|
ISO 11359-2 |
|
垂直 : 73 到 140°F
|
5.6E-5
|
in/in/°F
|
ISO 11359-2 |
|
导热系数
|
1.7
|
Btu·in/hr/ft²/°F
|
ISO 8302 |
|
RTI Elec
|
248
|
°F
|
UL 746B |
|
RTI Imp
|
248
|
°F
|
UL 746B |
|
RTI
|
284
|
°F
|
UL 746B |
|
表面电阻率
|
> 1.0E+15
|
ohms
|
IEC 60093 |
|
体积电阻率
|
> 1.0E+15
|
ohms·cm
|
IEC 60093 |
|
介电强度
|
|
|
|
|
0.0630 in, in Oil
|
610
|
V/mil
|
ASTM D149 |
|
0.126 in, in Air
|
470
|
V/mil
|
ASTM D149 |
|
0.0315 in, 在油中
|
890
|
V/mil
|
IEC 60243-1 |
|
0.0394 in 12
|
460
|
V/mil
|
IEC 60243-1 |
|
0.0630 in, 在油中
|
640
|
V/mil
|
IEC 60243-1 |
|
0.126 in, 在油中
|
430
|
V/mil
|
IEC 60243-1 |
|
相对电容率
|
|
|
IEC 60250 |
|
50 Hz
|
2.90
|
|
|
|
60 Hz
|
2.90
|
|
|
|
100 Hz
|
3.10
|
|
|
|
1 MHz
|
2.80
|
|
|
|
耗散因数
|
|
|
IEC 60250 |
|
50 Hz
|
1.0E-3
|
|
|
|
60 Hz
|
1.0E-3
|
|
|
|
100 Hz
|
2.0E-3
|
|
|
|
1 MHz
|
0.013
|
|
|
|
耐电弧性 13
|
PLC 6
|
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746A |
|
漏电起痕指数
|
|
|
IEC 60112 |
|
--
|
175
|
V
|
|
|
解决方案 B
|
100
|
V
|
|
|
高电弧燃烧指数(HAI) 14
|
PLC 0
|
|
UL 746A |
|
高压电弧抗点燃指数 (HVAR) (PLC)
|
PLC 6
|
|
UL 746A |
|
高电压电弧起痕速率 (HVTR)
|
PLC 4
|
|
UL 746A |
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746A |
|
UL 阻燃等级
|
|
|
UL 94 |
|
0.028 in
|
V-0
|
|
|
|
0.12 in
|
5VA
|
|
|
|
灼热丝易燃指数 (0.04 in)
|
1760
|
°F
|
IEC 60695-2-12 |
|
极限氧指数
|
30
|
%
|
ISO 4589-2 |
|
干燥温度
|
248
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 80
|
%
|
|
|
料筒后部温度
|
446 到 482
|
°F
|
|
|
料筒中部温度
|
464 到 491
|
°F
|
|
|
料筒前部温度
|
473 到 500
|
°F
|
|
|
射嘴温度
|
464 到 491
|
°F
|
|
|
加工（熔体）温度
|
473 到 500
|
°F
|
|
|
模具温度
|
122 到 167
|
°F
|
|
|
背压
|
43.5 到 102
|
psi
|
|
|
螺杆转速
|
50 到 100
|
rpm
|
|
|
排气孔深度
|
5.1E-4 到 9.8E-4
|
in
|
|
|
|
|