VALOX™ FR Resin 3706 - Americas
聚碳酸酯+PBT
产品说明:
VALOX 3706 is an unreinforced impact modified flame retardant Polybutylene Terephthalate/Polycarbonate (PBT/PC) injection moldable grade. It has excellent chemical resistance and a UL94V0@1.5mm and 5VA@2.49mm flame rating. This is a good candidate for outdoor enclosures.
|
材料状态
|
|
|
UL 黄卡 1
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
用途
|
- Electric Vehicle Applications
- Recreational Vehicle Applications
|
|
|
|
|
多点数据
|
- Coefficient of Thermal Expansion vs. Temperature (ASTM E831)
- Flexural DMA (ASTM D4065)
- Specific Heat vs. Temperature (ASTM D3417)
- Tensile Creep (ASTM D2990)
- Tensile Stress vs. Strain (ASTM D638)
- Thermal Conductivity vs. Temperature (ASTM E1530)
- Viscosity vs. Shear Rate (ASTM D3835)
|
|
Also Available In
|
|
|
密度 / 比重
|
1.30
|
|
ASTM D792 |
|
熔流率（熔体流动速率） (266°C/5.0 kg)
|
19
|
g/10 min
|
ASTM D1238 |
|
熔融体积流量（MVR） (265°C/5.0 kg)
|
17
|
cm³/10min
|
ISO 1133 |
|
收缩率
|
|
|
内部方法 |
|
垂直 : 0.126 in
|
1.2 到 1.4
|
%
|
|
|
流动 : 0.126 in
|
1.2 到 1.4
|
%
|
|
|
拉伸模量 2
|
284000
|
psi
|
ASTM D638 |
|
抗张强度 3
|
|
|
ASTM D638 |
|
屈服
|
6960
|
psi
|
|
|
断裂
|
5660
|
psi
|
|
|
伸长率 3
|
|
|
ASTM D638 |
|
屈服
|
6.0
|
%
|
|
|
断裂
|
50
|
%
|
|
|
弯曲模量 4 (1.97 in 跨距)
|
289000
|
psi
|
ASTM D790 |
|
弯曲强度 4 (屈服, 1.97 in 跨距)
|
11300
|
psi
|
ASTM D790 |
|
悬壁梁缺口冲击强度 (73°F)
|
12
|
ft·lb/in
|
ASTM D256 |
|
装有测量仪表的落镖冲击 (73°F, Total Energy)
|
434
|
in·lb
|
ASTM D3763 |
|
载荷下热变形温度
|
|
|
ASTM D648 |
|
66 psi, 未退火, 0.126 in
|
259
|
°F
|
|
|
264 psi, 未退火, 0.126 in
|
185
|
°F
|
|
|
维卡软化温度
|
275
|
°F
|
ASTM D1525 5 |
|
线形热膨胀系数
|
|
|
ASTM E831 |
|
流动 : -40 到 104°F
|
4.4E-5
|
in/in/°F
|
|
|
垂直 : -40 到 104°F
|
4.8E-5
|
in/in/°F
|
|
|
RTI Elec
|
212
|
°F
|
UL 746B |
|
RTI Imp
|
185
|
°F
|
UL 746B |
|
RTI
|
212
|
°F
|
UL 746B |
|
耐电弧性 6
|
PLC 6
|
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)
|
PLC 2
|
|
UL 746A |
|
高电弧燃烧指数(HAI) 7
|
PLC 0
|
|
UL 746A |
|
高电压电弧起痕速率 (HVTR)
|
PLC 4
|
|
UL 746A |
|
热丝引燃 (HWI)
|
PLC 2
|
|
UL 746A |
|
UL 阻燃等级
|
|
|
UL 94 |
|
0.06 in
|
V-0
|
|
|
|
0.10 in
|
5VA
|
|
|
|
干燥温度
|
248
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 80
|
%
|
|
|
料筒后部温度
|
464 到 491
|
°F
|
|
|
料筒中部温度
|
473 到 500
|
°F
|
|
|
料筒前部温度
|
482 到 509
|
°F
|
|
|
射嘴温度
|
473 到 500
|
°F
|
|
|
加工（熔体）温度
|
482 到 509
|
°F
|
|
|
模具温度
|
149 到 194
|
°F
|
|
|
背压
|
43.5 到 102
|
psi
|
|
|
螺杆转速
|
50 到 80
|
rpm
|
|
|
排气孔深度
|
9.8E-4 到 1.5E-3
|
in
|
|
|
|
|