我公司免费提供SGS UL COA物性表 请联系15017036185何生 微信同步 谢谢VALOX™ FR Resin 553U - Americas
聚碳酸酯+PBT
产品说明:
VALOX 553U is a 30% glass filled, UV stabilized flame retardant Polybutylene Terephthalate/Polycarbonate (PBT/PC) injection moldable grade. It has excellent chemical resistance and a UL94V0@0.86mm and 5VA@2.31mm flame rating. This is a good candidate for applications needing reduced shrinkage/warpage including appliance handles, spotlights, electric motors, and pump housings
|
材料状态
|
|
|
UL 黄卡 1
|
|
|
搜索 UL 黄卡
|
|
|
供货地区
|
|
|
用途
|
- Recreational Vehicle Applications
|
|
|
|
|
密度 / 比重
|
1.58
|
|
ASTM D792 |
|
特定体积
|
17.4
|
in³/lb
|
ASTM D792 |
|
收缩率
|
|
|
内部方法 |
|
垂直 : 0.0591 到 0.126 in
|
0.40 到 0.60
|
%
|
|
|
流动 : 0.0591 到 0.126 in
|
0.30 到 0.50
|
%
|
|
|
垂直 : 0.126 到 0.181 in
|
0.60 到 0.90
|
%
|
|
|
流动 : 0.126 到 0.181 in
|
0.50 到 0.80
|
%
|
|
|
吸水率 (24 hr, 73°F)
|
0.070
|
%
|
ASTM D570 |
|
室外适用性
|
f1
|
|
UL 746C |
|
洛氏硬度 (R 级)
|
118
|
|
ASTM D785 |
|
抗张强度 2 (断裂)
|
16000
|
psi
|
ASTM D638 |
|
弯曲模量 3 (1.97 in 跨距)
|
999000
|
psi
|
ASTM D790 |
|
弯曲强度 3 (断裂, 1.97 in 跨距)
|
26000
|
psi
|
ASTM D790 |
|
悬壁梁缺口冲击强度 (73°F)
|
1.6
|
ft·lb/in
|
ASTM D256 |
|
无缺口悬臂梁冲击 (73°F)
|
12
|
ft·lb/in
|
ASTM D4812 |
|
载荷下热变形温度
|
|
|
ASTM D648 |
|
66 psi, 未退火, 0.252 in
|
399
|
°F
|
|
|
264 psi, 未退火, 0.252 in
|
320
|
°F
|
|
|
线形热膨胀系数 - 流动
|
|
|
ASTM E831 |
|
-40 到 104°F
|
1.2E-5
|
in/in/°F
|
|
|
140 到 280°F
|
1.2E-5
|
in/in/°F
|
|
|
RTI Elec
|
257
|
°F
|
UL 746B |
|
RTI Imp
|
230
|
°F
|
UL 746B |
|
RTI
|
257
|
°F
|
UL 746B |
|
体积电阻率
|
4.3E+16
|
ohms·cm
|
ASTM D257 |
|
介电强度
|
|
|
ASTM D149 |
|
0.0630 in, in Oil
|
650
|
V/mil
|
|
|
0.126 in, in Air
|
480
|
V/mil
|
|
|
介电常数
|
|
|
ASTM D150 |
|
100 Hz
|
3.80
|
|
|
|
1 MHz
|
3.70
|
|
|
|
耗散因数
|
|
|
ASTM D150 |
|
100 Hz
|
2.0E-3
|
|
|
|
1 MHz
|
0.020
|
|
|
|
耐电弧性 4
|
PLC 6
|
|
ASTM D495 |
|
相比耐漏电起痕指数(CTI)
|
PLC 3
|
|
UL 746A |
|
高电弧燃烧指数(HAI) 5
|
PLC 3
|
|
UL 746A |
|
高电压电弧起痕速率 (HVTR)
|
PLC 3
|
|
UL 746A |
|
热丝引燃 (HWI)
|
PLC 1
|
|
UL 746A |
|
UL 阻燃等级
|
|
|
UL 94 |
|
0.03 in
|
V-0
|
|
|
|
0.09 in
|
5VA
|
|
|
|
极限氧指数
|
37
|
%
|
ASTM D2863 |
|
干燥温度
|
248
|
°F
|
|
|
干燥时间
|
3.0 到 4.0
|
hr
|
|
|
建议的最大水分含量
|
0.020
|
%
|
|
|
建议注射量
|
40 到 80
|
%
|
|
|
料筒后部温度
|
464 到 491
|
°F
|
|
|
料筒中部温度
|
473 到 500
|
°F
|
|
|
料筒前部温度
|
482 到 509
|
°F
|
|
|
射嘴温度
|
473 到 500
|
°F
|
|
|
加工（熔体）温度
|
482 到 509
|
°F
|
|
|
模具温度
|
149 到 194
|
°F
|
|
|
背压
|
43.5 到 102
|
psi
|
|
|
螺杆转速
|
50 到 80
|
rpm
|
|
|
|
|